The present work describes the preparation of chromium substituted magnetoplumbite ferrites from nitrate salts, and the effect of Cr on its structural and magnetic properties. Powders with nominal composition PbFe12-xCrxO19 (1.0 <= x <= 6.0) were obtained by thermal decomposition at 920 °C of coprecipitated hydroxide-carbonate mixed salts. A complete substitution of Fe3+ by Cr3+ was found and the influence of Cr on cell parameters, ordering temperatures and hysteretic properties are reported. The results are discussed and compared in connection with behaviour observed in isostructural Ba- and Sr-compounds.
Magnetic and Structural Characterisation of PbFe12-xCrxO19 (1.0 <= x <= 6.0) Hexaferrites Powders Obtained by Coprecipitation Method
B Watts;G Bocelli;
1997
Abstract
The present work describes the preparation of chromium substituted magnetoplumbite ferrites from nitrate salts, and the effect of Cr on its structural and magnetic properties. Powders with nominal composition PbFe12-xCrxO19 (1.0 <= x <= 6.0) were obtained by thermal decomposition at 920 °C of coprecipitated hydroxide-carbonate mixed salts. A complete substitution of Fe3+ by Cr3+ was found and the influence of Cr on cell parameters, ordering temperatures and hysteretic properties are reported. The results are discussed and compared in connection with behaviour observed in isostructural Ba- and Sr-compounds.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.