Studio di campioni prodotti con la tecnologia SLM da polvere SS316L attraverso misure termo-fisiche e microscopiche

In this work, we report a set of experimental results about several samples obtained by means of the SLM (selective laser melting) technology in the laboratories of CNR-ICMATE - Lecco unit. The specimens were obtained starting from SS316L powder. The characterization techniques concern the thermo-physical and microscopic properties: measurements of the electrical resistivity, evaluation of the thermal conduction coefficient, measurements of the density, study of the texturing, analysis of the melting pool. For all these characterization techniques, the influence of the orientation of the sample with respect to the working plane was evaluated.

In questo rapporto tecnico vengono riportati una serie di risultati di test di caratterizzazione di alcuni campioni realizzati mediante stampa additiva SLM (selective laser melting) nei laboratori dell'istituto ICMATE di Lecco, ottenuti da polvere di acciaio austenitico SS316L. Le tecniche di indagine sono state sia di tipo termo-fisico che microscopico: misure di resistenza elettrica, valutazione del coefficiente di conducibilità termica, misura di densità, valutazione della tessitura, studio della pozza di fusione. Per tutte queste tecniche è stato indagato l'effetto dell'orientazione dei campioni rispetto al piano di lavoro.