ZrB2 composites containing SiC chopped fibers were hot pressed at 1600-1900°C using different sintering aids. The change of sintering aid strongly affected the densification temperature and the mechanical properties of the composites. Addition of MoSi2 was detrimental to the final microstructure and properties, due to the high temperature needed to reach a full densification. Addition of ZrSi2 decreased the sintering temperature to 1650°C, and the resulting composite containing 20 vol.% fibers reached a toughness of 6.2 MPa m0.5.
SiC chopped fibers reinforced ZrB2: Effect of the sintering aid
Sciti Diletta;Silvestroni Laura;
2011
Abstract
ZrB2 composites containing SiC chopped fibers were hot pressed at 1600-1900°C using different sintering aids. The change of sintering aid strongly affected the densification temperature and the mechanical properties of the composites. Addition of MoSi2 was detrimental to the final microstructure and properties, due to the high temperature needed to reach a full densification. Addition of ZrSi2 decreased the sintering temperature to 1650°C, and the resulting composite containing 20 vol.% fibers reached a toughness of 6.2 MPa m0.5.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.