The precipitation kinetics of BaTiO3 was investigated using a 500 ml batch reactor. An acidic solution containing both cations was added to a NaOH solution at room temperature. A titanium-rich gel was instantaneously formed and the crystallisation of BaTiO3 occurred when the gel was heated above 70 °C. The precipitation process was modelled by a discretized population balance (DPB) approach for simultaneous nucleation and growth at unsteady state. A comparison between experimental and calculated data is presented.
Formation of BaTiO3 fine particels in aqueous solutions: experiments and modeling
M T Buscaglia;V Buscaglia;M Viviani;
2004
Abstract
The precipitation kinetics of BaTiO3 was investigated using a 500 ml batch reactor. An acidic solution containing both cations was added to a NaOH solution at room temperature. A titanium-rich gel was instantaneously formed and the crystallisation of BaTiO3 occurred when the gel was heated above 70 °C. The precipitation process was modelled by a discretized population balance (DPB) approach for simultaneous nucleation and growth at unsteady state. A comparison between experimental and calculated data is presented.File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
prod_228913-doc_56601.pdf
solo utenti autorizzati
Descrizione: Formation of BaTiO3 fine particels in aqueous solutions: experiments and modeling
Dimensione
290.58 kB
Formato
Adobe PDF
|
290.58 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.