Cu-alkali ion exchange in silicate glasses gives rise to a peculiar copper distribution, with the presence of both the Cu2+ and Cu+ oxidation states. Grazing incidence X-ray absorption near-edge structure spectroscopy and secondary ion mass spectrometry were performed on different ion-exchanged samples. The results show that the Cu2+/Cu+ ratio is strongly depth-dependent. The relative presence of the two species throughout the exchanged region turns out to be governed by their different diffusion regimes, while the chemistry of the red-ox process is shown to play a minor role. A phenomenological model is proposed to describe the diffusion process.
Copper diffusion in ion-exchanged soda-lime glass
2005
Abstract
Cu-alkali ion exchange in silicate glasses gives rise to a peculiar copper distribution, with the presence of both the Cu2+ and Cu+ oxidation states. Grazing incidence X-ray absorption near-edge structure spectroscopy and secondary ion mass spectrometry were performed on different ion-exchanged samples. The results show that the Cu2+/Cu+ ratio is strongly depth-dependent. The relative presence of the two species throughout the exchanged region turns out to be governed by their different diffusion regimes, while the chemistry of the red-ox process is shown to play a minor role. A phenomenological model is proposed to describe the diffusion process.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.