The structural properties and the room temperature luminescence of Er2O3 thin films deposited by RF magnetron sputtering have been studied. Films characterized by good morphological properties have been obtained by using a SiO2 interlayer between the film and the Si substrate. The evolution of the properties of the Er2O3 films due to rapid thermal annealing processes in O2 ambient performed at temperatures in the range 800-1200 °C has been investigated in details. The existence of well-defined annealing conditions (temperature of 1100 °C or higher) allowing to avoid the occurrence of extensive chemical reactions with the oxidized substrate has been demonstrated and an increase of the photoluminescence (PL) intensity by about a factor of 40 with respect to the as deposited material has been observed. The enhanced efficiency of the photon emission process has been correlated with the longer lifetime of the PL signal. The same annealing processes are less effective when Er2O3 is deposited on Si. In this latter case interfacial reactions and pit formation occur, leading to a material characterized by stronger non-radiative phenomena that limit the PL efficiency.
The influence of substrate on the properties of Er2O3 films grown by magnetron sputtering
Miritello M;Iacona F;Bongiorno C;Irrera A;Priolo F
2006
Abstract
The structural properties and the room temperature luminescence of Er2O3 thin films deposited by RF magnetron sputtering have been studied. Films characterized by good morphological properties have been obtained by using a SiO2 interlayer between the film and the Si substrate. The evolution of the properties of the Er2O3 films due to rapid thermal annealing processes in O2 ambient performed at temperatures in the range 800-1200 °C has been investigated in details. The existence of well-defined annealing conditions (temperature of 1100 °C or higher) allowing to avoid the occurrence of extensive chemical reactions with the oxidized substrate has been demonstrated and an increase of the photoluminescence (PL) intensity by about a factor of 40 with respect to the as deposited material has been observed. The enhanced efficiency of the photon emission process has been correlated with the longer lifetime of the PL signal. The same annealing processes are less effective when Er2O3 is deposited on Si. In this latter case interfacial reactions and pit formation occur, leading to a material characterized by stronger non-radiative phenomena that limit the PL efficiency.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.