We report grazing incidence x-ray scattering evidence for sharpening of the interface between amorphous Co60Fe20B20 and AlOx during in situ annealing below the Co60Fe20B20 crystallization temperature. Enhancement of the interference fringe amplitude in the specular scatter and the absence of changes in the diffuse scatter indicate that the sharpening is not a reduction in topological roughness but a reduction in the width of the chemical composition profile across the interface. The temperature at which the sharpening occurs corresponds to that at which a maximum is found in the tunneling magnetoresistance of magnetic tunnel junctions.
Interface sharpening in CoFeB magnetic tunnel junctions
A Lamperti;
2006
Abstract
We report grazing incidence x-ray scattering evidence for sharpening of the interface between amorphous Co60Fe20B20 and AlOx during in situ annealing below the Co60Fe20B20 crystallization temperature. Enhancement of the interference fringe amplitude in the specular scatter and the absence of changes in the diffuse scatter indicate that the sharpening is not a reduction in topological roughness but a reduction in the width of the chemical composition profile across the interface. The temperature at which the sharpening occurs corresponds to that at which a maximum is found in the tunneling magnetoresistance of magnetic tunnel junctions.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.