Reflectance versus incidence angle measurements have been performed from 5 to 152 nm on samples of SiC with a different C/Si ratio deposited with rf magnetron sputtering. The optical constants of the material at different wavelengths have been determined by using a curve-fitting technique of reflectance values versus incidence angle. Complementary measurements of the incident beam polarization, film thickness, surface roughness, and stoichiometry were performed to complete the analysis of the samples. (C) 2006 Optical Society of America.
Reflectance measurements and optical constants in the extreme ultraviolet-vacuum ultraviolet regions for SiC with a different C/Si ratio
F Frassetto;MG Pelizzo;A Giglia;S Nannarone
2006
Abstract
Reflectance versus incidence angle measurements have been performed from 5 to 152 nm on samples of SiC with a different C/Si ratio deposited with rf magnetron sputtering. The optical constants of the material at different wavelengths have been determined by using a curve-fitting technique of reflectance values versus incidence angle. Complementary measurements of the incident beam polarization, film thickness, surface roughness, and stoichiometry were performed to complete the analysis of the samples. (C) 2006 Optical Society of America.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.