We have examined the magnetoresistances of (La,Pr,Ca)MnO3 channel structures with different channel widths. The 500 nm channel showed an extremely sharp metallic transition from charge ordered insulator to ferromagnetic metal at low temperature, while the 10 and 1 mu m channels showed gradual metallic transitions. The sharpness of the metallic transition was increased from 1.3x10(2) T-1 in the 10 mu m channel to 3.5x10(4) T-1 in the 500 nm channel at 10 K. Such extremely sharp metallic transition can be accounted for electronic phase separation phenomena.
Digitalized magnetoresistance observed in (La,Pr,Ca)MnO3 nanochannel structures
Luca Pellegrino
2006
Abstract
We have examined the magnetoresistances of (La,Pr,Ca)MnO3 channel structures with different channel widths. The 500 nm channel showed an extremely sharp metallic transition from charge ordered insulator to ferromagnetic metal at low temperature, while the 10 and 1 mu m channels showed gradual metallic transitions. The sharpness of the metallic transition was increased from 1.3x10(2) T-1 in the 10 mu m channel to 3.5x10(4) T-1 in the 500 nm channel at 10 K. Such extremely sharp metallic transition can be accounted for electronic phase separation phenomena.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.