The titanium-rich PZT solid solution PbZr0.20Ti0.80O3 was studied under high pressure by X-ray diffraction and Raman spectroscopy. A series of low-symmetry phases were observed, including monoclinic (space groups Cm and Cc) and triclinic forms (space groups F1 and F1 ?) in PbZr0.20Ti0.80O3. High pressure Raman spectra obtained are consistent with a monoclinic (Cc)-triclinic (F1) phase transition involving a soft mode at 9 GPa, in agreement with the change in compressibility detected by X-ray diffraction. The strong Raman spectra observed in the paraelectric phase can also be explained by the triclinic F 1 ? symmetry.
Pressure-induced low symmetry phases in Ti-rich lead zirconate.
2005
Abstract
The titanium-rich PZT solid solution PbZr0.20Ti0.80O3 was studied under high pressure by X-ray diffraction and Raman spectroscopy. A series of low-symmetry phases were observed, including monoclinic (space groups Cm and Cc) and triclinic forms (space groups F1 and F1 ?) in PbZr0.20Ti0.80O3. High pressure Raman spectra obtained are consistent with a monoclinic (Cc)-triclinic (F1) phase transition involving a soft mode at 9 GPa, in agreement with the change in compressibility detected by X-ray diffraction. The strong Raman spectra observed in the paraelectric phase can also be explained by the triclinic F 1 ? symmetry.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.