MnAs thin films were grown by metalorganic vapour-phase epitaxy (MOVPE) on GaAs(0 0 1), Si(0 0 1) and oxidised silicon substrates. All films are crystalline and contain only the ferromagnetic a-MnAs phase. X-ray diffraction (XRD) and atomic force microscopy (AFM) measurements show that films on GaAs(0 0 1) have strong preferential orientation, developing elongated grains parallel to [1 1 0] GaAs while films on bare and oxidised Si are polycrystalline with irregular-shaped, randomly oriented grains. Magneto-optic Kerr effect (MOKE) measurements show good magnetic properties for films on GaAs, such as strong in-plane anisotropy and squareness of the hysteresis loop in the easy direction. A Curie temperature of 340 K, remarkably higher than the bulk material (315 K), was found for a 65 nm thick film on GaAs. Films grown on bare and oxidised silicon wafers had lower Curie temperature and were magnetically isotropic.
Growth and characterization of ferromagnetic MnAs films on different semiconductor substrates
I Bergenti;G Rossetto;P Zanella;V Dediu;M Natali
2007
Abstract
MnAs thin films were grown by metalorganic vapour-phase epitaxy (MOVPE) on GaAs(0 0 1), Si(0 0 1) and oxidised silicon substrates. All films are crystalline and contain only the ferromagnetic a-MnAs phase. X-ray diffraction (XRD) and atomic force microscopy (AFM) measurements show that films on GaAs(0 0 1) have strong preferential orientation, developing elongated grains parallel to [1 1 0] GaAs while films on bare and oxidised Si are polycrystalline with irregular-shaped, randomly oriented grains. Magneto-optic Kerr effect (MOKE) measurements show good magnetic properties for films on GaAs, such as strong in-plane anisotropy and squareness of the hysteresis loop in the easy direction. A Curie temperature of 340 K, remarkably higher than the bulk material (315 K), was found for a 65 nm thick film on GaAs. Films grown on bare and oxidised silicon wafers had lower Curie temperature and were magnetically isotropic.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.