Three new azo-polyurethanes containing the s-triazolo[3,4-b]thiadiazole heterocycle have been prepared and characterized. The polymers showed glass transition temperatures between 183 °C and 232 °C and a moderate to good thermal stability in air. The thermal cis-trans isomerization around the azo group was analyzed in solution and the kinetic constant of this process was calculated. One of the synthesized polymers was processed in form of thin films (thickness was 1.2 lm) and some experiments of optical laser writing were performed on it: three different surface relief gratings (SRGs) structures were realized at micrometer scale (a square, a concentric square pattern and a grating) indi- cating this polymer as an interesting candidate for the azo-lithography.
Cis-trans isomerization and optical laser writing in new heterocycle based azo-polyurethane
2012
Abstract
Three new azo-polyurethanes containing the s-triazolo[3,4-b]thiadiazole heterocycle have been prepared and characterized. The polymers showed glass transition temperatures between 183 °C and 232 °C and a moderate to good thermal stability in air. The thermal cis-trans isomerization around the azo group was analyzed in solution and the kinetic constant of this process was calculated. One of the synthesized polymers was processed in form of thin films (thickness was 1.2 lm) and some experiments of optical laser writing were performed on it: three different surface relief gratings (SRGs) structures were realized at micrometer scale (a square, a concentric square pattern and a grating) indi- cating this polymer as an interesting candidate for the azo-lithography.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.