A two-step plasma enhanced chemical vapor deposition procedure has been developed to produce high quality SixNyHz films for quantum cascade laser applications. The procedure consists in exposing the GaAs substrate to a controlled N-2 plasma previous to the silicon nitride film deposition. The pre-treatment causes the formation of a thin GaN film that passivates the GaAs wafer. The method has been optimized varying RF power, N-2 flow rate and process time of the pre-treatments and monitoring their effects on the resulting chemical composition and dielectric properties of the nitride overlayers, by means of infrared spectroscopy, X-ray photoelectron spectroscopy and electric characterizations. A narrow window in the pre-treatment RF power, N-2 flux and time values, improves the composition, structural and dielectric properties of the silicon nitride overlayers. The best result has been found depositing the silicon nitride films on GaAs wafer after 2 min of N-2 plasma treatment with a power of 20 W and a 50 cm(3)/min flow rate. (C) 2007 Elsevier B.V. All rights reserved.
Influence of substrate pre-treatments on the growth of SixNyHz thin films by plasma enhanced chemical vapor deposition
Di Franco C;Scamarcio G
2008
Abstract
A two-step plasma enhanced chemical vapor deposition procedure has been developed to produce high quality SixNyHz films for quantum cascade laser applications. The procedure consists in exposing the GaAs substrate to a controlled N-2 plasma previous to the silicon nitride film deposition. The pre-treatment causes the formation of a thin GaN film that passivates the GaAs wafer. The method has been optimized varying RF power, N-2 flow rate and process time of the pre-treatments and monitoring their effects on the resulting chemical composition and dielectric properties of the nitride overlayers, by means of infrared spectroscopy, X-ray photoelectron spectroscopy and electric characterizations. A narrow window in the pre-treatment RF power, N-2 flux and time values, improves the composition, structural and dielectric properties of the silicon nitride overlayers. The best result has been found depositing the silicon nitride films on GaAs wafer after 2 min of N-2 plasma treatment with a power of 20 W and a 50 cm(3)/min flow rate. (C) 2007 Elsevier B.V. All rights reserved.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.