Films of the molecular nanomagnet Mn12ac with thicknesses spanning the nm to mm range have been deposited using a customised vacuum spray deposition technique. The films have been characterized by AFM, XPS, magnetic and magneto-optical measurements, indicating that the deposition procedure does not damage the Mn12ac molecules. As a result, the films show magnetic properties similar to those of the parent molecular material down to the nm thickness range, as revealed by magneto-optical methods. Vacuum spray deposition therefore represents a promising approach for the preparation under controlled vacuum conditions of ultrathin films of molecular nanomagnets supported on transparent dielectric substrates, making possible the magneto-optical readout of the magnetisation state of the Mn12ac film.
Optically addressable single molecule magnet behaviour of vacuum-sprayed ultrathin films
R Moroni;R Buzio;L Cavigli;
2008
Abstract
Films of the molecular nanomagnet Mn12ac with thicknesses spanning the nm to mm range have been deposited using a customised vacuum spray deposition technique. The films have been characterized by AFM, XPS, magnetic and magneto-optical measurements, indicating that the deposition procedure does not damage the Mn12ac molecules. As a result, the films show magnetic properties similar to those of the parent molecular material down to the nm thickness range, as revealed by magneto-optical methods. Vacuum spray deposition therefore represents a promising approach for the preparation under controlled vacuum conditions of ultrathin films of molecular nanomagnets supported on transparent dielectric substrates, making possible the magneto-optical readout of the magnetisation state of the Mn12ac film.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.