The angular dependencies of the critical current density, J(c)(theta), for superconducting Nb/Pd multilayers which show, in parallel magnetic field, a pronounced peak effect, were investigated (here theta is defined as the angle from the plane parallel to the sample surface). We have demonstrated that the procedure of measurements is an important factor for the J(c)(theta) shape. When rotating the sample in a fixed magnetic field H, it was found that the external field direction at which the maximum of J(c) was obtained form an angle different from zero with respect to the planar direction. The angular position of the maximum depends on the external magnetic field, as well as on the initial conditions under which the samples were kept. It is found that the more intense the peak effect is on the J(c)(H) curves, the larger the angular shift is of J(c)(theta) in these structures. The results are explained in terms of the magnetic field suppression of the percolation currents in a weak-link network. Flux trapped within grains by the flux pinning processes is relatively stable at low fields and its contributions to the transport current suppression add vectorially to the applied field.
Angular effects of the critical current in Nb/Pd multilayers
Attanasio C;Cirillo C;
2006
Abstract
The angular dependencies of the critical current density, J(c)(theta), for superconducting Nb/Pd multilayers which show, in parallel magnetic field, a pronounced peak effect, were investigated (here theta is defined as the angle from the plane parallel to the sample surface). We have demonstrated that the procedure of measurements is an important factor for the J(c)(theta) shape. When rotating the sample in a fixed magnetic field H, it was found that the external field direction at which the maximum of J(c) was obtained form an angle different from zero with respect to the planar direction. The angular position of the maximum depends on the external magnetic field, as well as on the initial conditions under which the samples were kept. It is found that the more intense the peak effect is on the J(c)(H) curves, the larger the angular shift is of J(c)(theta) in these structures. The results are explained in terms of the magnetic field suppression of the percolation currents in a weak-link network. Flux trapped within grains by the flux pinning processes is relatively stable at low fields and its contributions to the transport current suppression add vectorially to the applied field.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.