Zinc tellurite glasses of compositions 19ZnO80TeO21Ln2O3 with Ln=Eu, Er, Nd and Tm were prepared by melt quenching. The absorption spectra were measured and from the experimental oscillator strengths of the f-f transitions the JuddOfelt parameters .?.. were obtained. The values of the.?..parameters are in the range usually observed for oxide glasses. For Nd3+ and Er3+, luminescence spectra in the near infrared were measured and the stimulated emission cross sections ..?.. were evaluated for some laser transitions. The high values of ..?.., especially for Nd3+, make them possible candidates for optical applications. Fluorescence line narrowing (FLN) spectra of the Eu3+ doped glass were measured at 20 K, and the energies of the Stark components of the 7F1 and 7F2 states were obtained. A crystal field analysis was carried out assuming a C2v site symmetry. The behaviour of the crystal field ratios B22/B20 and B44/B40 agrees reasonably well with the values calculated using the geometric model proposed by Brecher and Riseberg. The crystal field strength at the Eu3+ sites appears to be very low compared to other oxide glasses.
Optical spectroscopy of lanthanide ions in ZnO-TeO2 glasses
2001
Abstract
Zinc tellurite glasses of compositions 19ZnO80TeO21Ln2O3 with Ln=Eu, Er, Nd and Tm were prepared by melt quenching. The absorption spectra were measured and from the experimental oscillator strengths of the f-f transitions the JuddOfelt parameters .?.. were obtained. The values of the.?..parameters are in the range usually observed for oxide glasses. For Nd3+ and Er3+, luminescence spectra in the near infrared were measured and the stimulated emission cross sections ..?.. were evaluated for some laser transitions. The high values of ..?.., especially for Nd3+, make them possible candidates for optical applications. Fluorescence line narrowing (FLN) spectra of the Eu3+ doped glass were measured at 20 K, and the energies of the Stark components of the 7F1 and 7F2 states were obtained. A crystal field analysis was carried out assuming a C2v site symmetry. The behaviour of the crystal field ratios B22/B20 and B44/B40 agrees reasonably well with the values calculated using the geometric model proposed by Brecher and Riseberg. The crystal field strength at the Eu3+ sites appears to be very low compared to other oxide glasses.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.