The cobalt-chromium-molybdenum alloys are characterized by a high resistance to wear and corrosion, as well as good mechanical properties, allowing their use in the substitution of hip and knee joints. Five alloys were used as substrates for a coating deposition by a thermal treatment in molten salts, as reported elsewhere, in order to form a tantalum-rich coating on the sample surface, able to improve the biocompatibility and wear resistance of the materials. However, the temperature (970 °C), reached during this process, is considered critical for the phase transformation of the Co-based alloys. The aim of this work is the evaluation of the temperature effects on the structure, microstructure, mechanical and tribological properties of the considered substrates, after the removal of the coating by polishing. The substrates are characterized through X-ray diffraction (XRD), scanning electron microscopy with energy dispersion spectrometry (SEM-EDS) and profilometry. The mechanical behavior is evaluated by the macro- and micro-hardness and bending tests, whereas the tribological properties are analyzed through a ball on disc test. A comparison between the as-received alloys and thermal treated substrates is reported. The biocompatibility feature is not reported in this work. The substrate crystalline structure changed during the heat treatment, inducing the formation of the hexagonal cobalt phase and the decrement of the cubic one. This crystallographic modification does not seem to influence the tribological behavior of the substrates. On the contrary, it affects the strength and ductility of the substrates.
Characterization of Co-Cr-Mo alloys after a thermal treatment for high wear resistance
MG Faga
2012
Abstract
The cobalt-chromium-molybdenum alloys are characterized by a high resistance to wear and corrosion, as well as good mechanical properties, allowing their use in the substitution of hip and knee joints. Five alloys were used as substrates for a coating deposition by a thermal treatment in molten salts, as reported elsewhere, in order to form a tantalum-rich coating on the sample surface, able to improve the biocompatibility and wear resistance of the materials. However, the temperature (970 °C), reached during this process, is considered critical for the phase transformation of the Co-based alloys. The aim of this work is the evaluation of the temperature effects on the structure, microstructure, mechanical and tribological properties of the considered substrates, after the removal of the coating by polishing. The substrates are characterized through X-ray diffraction (XRD), scanning electron microscopy with energy dispersion spectrometry (SEM-EDS) and profilometry. The mechanical behavior is evaluated by the macro- and micro-hardness and bending tests, whereas the tribological properties are analyzed through a ball on disc test. A comparison between the as-received alloys and thermal treated substrates is reported. The biocompatibility feature is not reported in this work. The substrate crystalline structure changed during the heat treatment, inducing the formation of the hexagonal cobalt phase and the decrement of the cubic one. This crystallographic modification does not seem to influence the tribological behavior of the substrates. On the contrary, it affects the strength and ductility of the substrates.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.