We report the synthesis under pressure, the critical temperature and the structural characteristics of YSr2Cu3Ow. The compound does not form at normal pressure, but, once formed, can be retained at normal pressure in a metastable state. The synthesis was carried out in a multi-anvil apparatus at 30 kBars and 1050 degreesC. The as-prepared sample was found to become superconductor with a Te of approximate to 63K. Tc increased up to approximate to 70 K after annealing in oxygen at 290 degreesC. The refinement of the neutron diffraction data indicated that the as prepared YSr2Cu3Ow. is tetragonal (a=3.7855 Angstrom and c=11.386 Angstrom) and the oxygen content, w, is approximate to 6.84.
We report the synthesis under pressure, the critical temperature and the structural characteristics of YSr2Cu3Ow. The compound does not form at normal pressure, but, once formed, can be retained at normal pressure in a metastable state. The synthesis was carried out in a multi-anvil apparatus at 30 kBars and 1050 degreesC. The as-prepared sample was found to become superconductor with a Te of approximate to 63K. Tc increased up to approximate to 70 K after annealing in oxygen at 290 degreesC. The refinement of the neutron diffraction data indicated that the as prepared YSr2Cu3Ow. is tetragonal (a=3.7855 Angstrom and c=11.386 Angstrom) and the oxygen content, w, is approximate to 6.84.
High pressure synthesis and characterization of YSr2Cu3OW
Gilioli;Besagni;Licci;
2000
Abstract
We report the synthesis under pressure, the critical temperature and the structural characteristics of YSr2Cu3Ow. The compound does not form at normal pressure, but, once formed, can be retained at normal pressure in a metastable state. The synthesis was carried out in a multi-anvil apparatus at 30 kBars and 1050 degreesC. The as-prepared sample was found to become superconductor with a Te of approximate to 63K. Tc increased up to approximate to 70 K after annealing in oxygen at 290 degreesC. The refinement of the neutron diffraction data indicated that the as prepared YSr2Cu3Ow. is tetragonal (a=3.7855 Angstrom and c=11.386 Angstrom) and the oxygen content, w, is approximate to 6.84.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.