Scanning tunneling spectroscopy suggests the formation of a two dimensional electron gas (2DEG) on the TiO2 terminated surface of undoped SrTiO3 single crystals annealed at temperature lower than 400 °C in ultra high vacuum conditions. Low energy electron diffraction indicates that the 2D metallic SrTiO3 surface is not structurally reconstructed, suggesting that non-ordered oxygen vacancies created in the annealing process introduce carriers leading to an electronic reconstruction. The experimental results are interpreted in a frame of competition between oxygen diffusion from the bulk to the surface and oxygen loss from the surface itself.
Observation of a two-dimensional electron gas at the surface of annealed SrTiO3 single crystals by scanning tunneling spectroscopy
R Di Capua;F Miletto Granozio;U Scotti di Uccio;R Vaglio;M Salluzzo
2012
Abstract
Scanning tunneling spectroscopy suggests the formation of a two dimensional electron gas (2DEG) on the TiO2 terminated surface of undoped SrTiO3 single crystals annealed at temperature lower than 400 °C in ultra high vacuum conditions. Low energy electron diffraction indicates that the 2D metallic SrTiO3 surface is not structurally reconstructed, suggesting that non-ordered oxygen vacancies created in the annealing process introduce carriers leading to an electronic reconstruction. The experimental results are interpreted in a frame of competition between oxygen diffusion from the bulk to the surface and oxygen loss from the surface itself.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.