CrCl2·(dmpe)2-MAO gives crystalline 1,2 syndiotactic polymers from butadiene and 3,4 atactic polymers from isoprene. Butadiene-isoprene copolymerization gives copolymers in which butadiene and isoprene units have respectively a 1,2 and a 3,4 structure. Copolymers with less than 20% isoprene are crystalline, their melting point decreasing from ca. 160°C to ca. 50°C with increasing isoprene content. This makes possible to obtain 1,2 syndiotactic polybutadiene with controlled melting point. Copolymers with more than 20% isoprene are amorphous, with a glass transition temperature in the range 2¸5°C. Copolymer microstructure was determined by 13C NMR.
1,2 syndiotactic polybutadiene of controlled crystallinity by butadiene-isoprene copolymerization with CrCl2(dmpe)2-MAO
G Ricci;F Bertini;
2002
Abstract
CrCl2·(dmpe)2-MAO gives crystalline 1,2 syndiotactic polymers from butadiene and 3,4 atactic polymers from isoprene. Butadiene-isoprene copolymerization gives copolymers in which butadiene and isoprene units have respectively a 1,2 and a 3,4 structure. Copolymers with less than 20% isoprene are crystalline, their melting point decreasing from ca. 160°C to ca. 50°C with increasing isoprene content. This makes possible to obtain 1,2 syndiotactic polybutadiene with controlled melting point. Copolymers with more than 20% isoprene are amorphous, with a glass transition temperature in the range 2¸5°C. Copolymer microstructure was determined by 13C NMR.File | Dimensione | Formato | |
---|---|---|---|
prod_210876-doc_55925.pdf
non disponibili
Descrizione: 1,2 syndiotactic polybutadiene of controlled crystallinity
Dimensione
94.62 kB
Formato
Adobe PDF
|
94.62 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.