gamma-Al2O3samples, both pure and Cr doped, were prepared by heating at 470°C sol - gel precursors obtained by using aluminum tri-sec-butoxide [Al(OC4H9)3] as the starting compound. The samples were characterised for phase composition (X-ray diffraction) and surface area (BET). Electrochemical determinations of the double layer reactivity of the pure and doped oxides were performed both by surface charge and by electrokinetic sonic amplitude (ESA) determinations. The interfacial electrostatic response is discussed and analysed also with reference to the sample surface state obtained by X-ray photoelectron spectroscopy (XPS).
Chromium doped gamma-Al2O3 powders. Features of the electrical double layer and state of the surface species
Galassi;
2000
Abstract
gamma-Al2O3samples, both pure and Cr doped, were prepared by heating at 470°C sol - gel precursors obtained by using aluminum tri-sec-butoxide [Al(OC4H9)3] as the starting compound. The samples were characterised for phase composition (X-ray diffraction) and surface area (BET). Electrochemical determinations of the double layer reactivity of the pure and doped oxides were performed both by surface charge and by electrokinetic sonic amplitude (ESA) determinations. The interfacial electrostatic response is discussed and analysed also with reference to the sample surface state obtained by X-ray photoelectron spectroscopy (XPS).File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.