The solid solution of the ferroelectric relaxor (Na1/2Bi 1/2)TiO3 with BaTiO3, (1-x) NBT-x BT (NBT-BT) shows a morphotropic phase boundary with enhanced properties at x = 6.06-0.07. We have prepared targets of (1-x) NBT-x BT with x = 0.06 by solid state reaction and sintering at 1200°C, up to a final relative density of 97.8%. Films from these targets have been deposited on MgO substrates by pulsed laser deposition, in different substrate temperature and heating rate conditions. First results obtained from structural, AFM and electrical characterization are reported. The obtained films are polycrystalline perovskite with a slight (100) orientation. High relative dielectric constant, of about 1300, have been obtained. © EDP Sciences, Les Ulis.
Ferroelectric (Na1/2Bi1/2)TiO3-BaTiO 3 thin films obtained by pulsed laser deposition
Galassi;
2005
Abstract
The solid solution of the ferroelectric relaxor (Na1/2Bi 1/2)TiO3 with BaTiO3, (1-x) NBT-x BT (NBT-BT) shows a morphotropic phase boundary with enhanced properties at x = 6.06-0.07. We have prepared targets of (1-x) NBT-x BT with x = 0.06 by solid state reaction and sintering at 1200°C, up to a final relative density of 97.8%. Films from these targets have been deposited on MgO substrates by pulsed laser deposition, in different substrate temperature and heating rate conditions. First results obtained from structural, AFM and electrical characterization are reported. The obtained films are polycrystalline perovskite with a slight (100) orientation. High relative dielectric constant, of about 1300, have been obtained. © EDP Sciences, Les Ulis.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.