The heating-induced crystallization process of Mg-Ni-Fe amorphous alloys was studied by anelastic spectroscopy and differential scanning calorimetry in the temperature range 100-500 K. The crystallization is obtained through several progressive non-reversible steps, detected by changes in the Young's modulus and concomitant irreversible peaks in the elastic energy loss curve. A systematic study of the anelastic spectrum measured on samples at different crystallization steps was carried out. Moreover, a non-thermally activated anelastic peak was observed at 215 K which is attributed to a dynamical process connected to the simultaneous presence of different phases.
The crystallization process of Mg-Ni-Fe alloys
Palumbo O.;Paolone A.;
2009
Abstract
The heating-induced crystallization process of Mg-Ni-Fe amorphous alloys was studied by anelastic spectroscopy and differential scanning calorimetry in the temperature range 100-500 K. The crystallization is obtained through several progressive non-reversible steps, detected by changes in the Young's modulus and concomitant irreversible peaks in the elastic energy loss curve. A systematic study of the anelastic spectrum measured on samples at different crystallization steps was carried out. Moreover, a non-thermally activated anelastic peak was observed at 215 K which is attributed to a dynamical process connected to the simultaneous presence of different phases.| File | Dimensione | Formato | |
|---|---|---|---|
|
prod_267431-doc_74143.pdf
solo utenti autorizzati
Descrizione: The crystallization process of Mg-Ni-Fe alloys
Tipologia:
Versione Editoriale (PDF)
Licenza:
NON PUBBLICO - Accesso privato/ristretto
Dimensione
495.07 kB
Formato
Adobe PDF
|
495.07 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.