Four series of Ni(51.4)Mn(28.3)Ga(20.3)/substrate thin film composites, where the substrate is either Si(100), MgO(100), alumina or Mo foil, and two series of Ni(53.5)Mn(23.8)Ga(22.7)/substrate composites where the substrate is either alumina or Mo foil, with different film thicknesses varying from 0.1 to 5 mu m have been studied in the cubic phase by XRD stress measurements. The values of residual stresses are found to be dependent on both substrate and film thickness. In the submicron range, a correlation between thickness dependencies of residual stress and transformation temperatures is experimentally obtained. The temperature dependence of the d-spacing d(220) is studied for the films deposited on Si(100).
Residual stress in Ni-Mn-Ga thin films deposited on different substrates.
2008
Abstract
Four series of Ni(51.4)Mn(28.3)Ga(20.3)/substrate thin film composites, where the substrate is either Si(100), MgO(100), alumina or Mo foil, and two series of Ni(53.5)Mn(23.8)Ga(22.7)/substrate composites where the substrate is either alumina or Mo foil, with different film thicknesses varying from 0.1 to 5 mu m have been studied in the cubic phase by XRD stress measurements. The values of residual stresses are found to be dependent on both substrate and film thickness. In the submicron range, a correlation between thickness dependencies of residual stress and transformation temperatures is experimentally obtained. The temperature dependence of the d-spacing d(220) is studied for the films deposited on Si(100).I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.