70SiO230HfO2 planar waveguides, doped with Er3+ concentrations ranging from 0.3 to 1 mol %, were prepared by sol-gel route, using dip-coating deposition on silica glass substrates. The waveguides show high densification degree, effective intermingling of the two components of the film, and uniform surface morphology. Propagation losses of about 1 dB/cm were measured at 632.8 nm. When pumped with 987 or 514.5 nm continuous-wave laser light, the waveguides show the 4I13/2-->4I15/2 emission band with a bandwidth of 48 nm. The spectral features are found independent both on erbium content and excitation wavelength. The 4I13/2 level decay curves presented a single-exponential profile, with a lifetime between 2.9 and 5.0 ms, depending on the erbium concentration.
Sol-gel Er-doped SiO2?HfO2 Planar Waveguides: A Viable System for 1.5 µm Application
Chiasera A;Pelli S;
2002
Abstract
70SiO230HfO2 planar waveguides, doped with Er3+ concentrations ranging from 0.3 to 1 mol %, were prepared by sol-gel route, using dip-coating deposition on silica glass substrates. The waveguides show high densification degree, effective intermingling of the two components of the film, and uniform surface morphology. Propagation losses of about 1 dB/cm were measured at 632.8 nm. When pumped with 987 or 514.5 nm continuous-wave laser light, the waveguides show the 4I13/2-->4I15/2 emission band with a bandwidth of 48 nm. The spectral features are found independent both on erbium content and excitation wavelength. The 4I13/2 level decay curves presented a single-exponential profile, with a lifetime between 2.9 and 5.0 ms, depending on the erbium concentration.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.