In this work, the relationships between composition and properties of Ny6/EVOH system were examined by means of several techniques and the results were interpreted in terms of level of compatibility. Blends of different ratio of Ny6 and EVOH have been processed in a laboratory-based film blowing extrusion apparatus. Rheological measurements, FTIR and morphological analysis, and thermal and mechanical properties were carried out. Peculiar rheological, thermal, and mechanical behaviors were observed for the blend containing 25% by weight of EVOH. At this composition, FTIR analysis has pointed out that a minimum in molecular motion is achieved as a consequence of a maximum interaction of the polar groups (amide groups of Ny6 and hydroxyl groups of EVOH) involved. Moreover, gas permeability measurements on the blown films have been performed at T 5 30°C
Influence of composition on properties of nylon 6/EVOH blends
P Russo;M Malinconico;P Laurienzo
1999
Abstract
In this work, the relationships between composition and properties of Ny6/EVOH system were examined by means of several techniques and the results were interpreted in terms of level of compatibility. Blends of different ratio of Ny6 and EVOH have been processed in a laboratory-based film blowing extrusion apparatus. Rheological measurements, FTIR and morphological analysis, and thermal and mechanical properties were carried out. Peculiar rheological, thermal, and mechanical behaviors were observed for the blend containing 25% by weight of EVOH. At this composition, FTIR analysis has pointed out that a minimum in molecular motion is achieved as a consequence of a maximum interaction of the polar groups (amide groups of Ny6 and hydroxyl groups of EVOH) involved. Moreover, gas permeability measurements on the blown films have been performed at T 5 30°CI documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.