The refractive indexes, material attenuation and damage fractions of a multi-step ion implanted Lithium Niobate (LiNbO3) waveguide were analyzed as functions of the annealing temperatures. An almost flat damage depth profile was designed to reduce the uncertainties related to the indexes profile shape, thus providing a better test-case for the characterizations. The measurements performed on the fabricated optical waveguides confirmed the predicted step-index profiles showing that the light is confined inside the damaged layer. The low measured attenuation (less than 0.8 dB/cm @ 632.8 nm) makes the obtained waveguide attractive for device fabrication.
Step-index optical waveguide produced by multistep ion implantation in LiNbO3
M Bianconi;G G Bentini
2012
Abstract
The refractive indexes, material attenuation and damage fractions of a multi-step ion implanted Lithium Niobate (LiNbO3) waveguide were analyzed as functions of the annealing temperatures. An almost flat damage depth profile was designed to reduce the uncertainties related to the indexes profile shape, thus providing a better test-case for the characterizations. The measurements performed on the fabricated optical waveguides confirmed the predicted step-index profiles showing that the light is confined inside the damaged layer. The low measured attenuation (less than 0.8 dB/cm @ 632.8 nm) makes the obtained waveguide attractive for device fabrication.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.