Si3N4-composite materials containing different amounts of MoSi2 were produced by hot-pressing. MoSi2 particles (mean size 0.8 mm) were homogeneously dispersed within a nanostructured Si3N4 matrix (mean grain size < 0.2 mm). The influence of MoSi2 inclusions on the microstructure, and electrical and mechanical properties of the composites is discussed and compared to the properties of monolithic Si3N4. As a result of the refined matrix microstructure and presence of ductile inclusions, these materials possess good mechanical properties, with bending strengths up to 1130 MPa (RT) and 880 MPa (1000°C) and fracture toughnesses up to 8 MPa·m½. Electrical resistivity is ~10-3 W·cm.
Microstructure and properties of Si3N4-MoSi2 composites
A. Bellosi;S. Guicciardi o Guizzardi;D. Sciti
2002
Abstract
Si3N4-composite materials containing different amounts of MoSi2 were produced by hot-pressing. MoSi2 particles (mean size 0.8 mm) were homogeneously dispersed within a nanostructured Si3N4 matrix (mean grain size < 0.2 mm). The influence of MoSi2 inclusions on the microstructure, and electrical and mechanical properties of the composites is discussed and compared to the properties of monolithic Si3N4. As a result of the refined matrix microstructure and presence of ductile inclusions, these materials possess good mechanical properties, with bending strengths up to 1130 MPa (RT) and 880 MPa (1000°C) and fracture toughnesses up to 8 MPa·m½. Electrical resistivity is ~10-3 W·cm.File | Dimensione | Formato | |
---|---|---|---|
prod_292951-doc_84023.pdf
solo utenti autorizzati
Descrizione: Microstructure and properties of Si3N4-MoSi2 composites
Tipologia:
Versione Editoriale (PDF)
Licenza:
NON PUBBLICO - Accesso privato/ristretto
Dimensione
1.35 MB
Formato
Adobe PDF
|
1.35 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.