The composition and spatial distribution of different Ti-Si phases formed by irradiation of a 5 ML Ti film deposited on Si(1 0 0) with visible and UV short laser pulses was studied employing scanning XPS microscopy with lateral resolution of 0.12 ?m. The lineshape of the Ti2p and Si2p spectra and the Ti2p and Si2p maps of the laser processed area have revealed that TiSi is produced in the external region of the laser spots, where the surface temperature does not exceed 500°C, whereas in the central area TiSi2 forms. The synthesis of more diluted alloys is consistent with the thermal gradient existing on the Ti/Si(0 0 1) surface during laser irradiation. © 2001 Elsevier Science B.V.
Visible and UV pulsed laser processing of the Ti/Si(0 0 1) interface studied by XPS microscopy with synchrotron radiation
Larciprete;La;La;
2001
Abstract
The composition and spatial distribution of different Ti-Si phases formed by irradiation of a 5 ML Ti film deposited on Si(1 0 0) with visible and UV short laser pulses was studied employing scanning XPS microscopy with lateral resolution of 0.12 ?m. The lineshape of the Ti2p and Si2p spectra and the Ti2p and Si2p maps of the laser processed area have revealed that TiSi is produced in the external region of the laser spots, where the surface temperature does not exceed 500°C, whereas in the central area TiSi2 forms. The synthesis of more diluted alloys is consistent with the thermal gradient existing on the Ti/Si(0 0 1) surface during laser irradiation. © 2001 Elsevier Science B.V.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.