We report on the isotropic pinning obtained in epitaxial Fe(Se,Te) thin films grown on CaF2(001) substrate. High critical current density values - larger than 1 MA/cm2 in self field and liquid helium - are reached together with a very weak dependence on the magnetic field and a complete isotropy. Analysis through transmission electron microscopy evidences the presence of defects looking like lattice disorder at a very small scale, between 5 and 20 nm, which are thought to be responsible for such isotropic behavior in contrast to what was observed on SrTiO3, where defects parallel to the c-axis enhance pinning in that direction. © 2013 AIP Publishing LLC.
Highly effective and isotropic pinning in epitaxial Fe(Se,Te) thin films grown on CaF2 substrates
Braccini;Va;Kawale;Bellingeri;Pellegrino;Putti;Ferdeghini;Ca
2013
Abstract
We report on the isotropic pinning obtained in epitaxial Fe(Se,Te) thin films grown on CaF2(001) substrate. High critical current density values - larger than 1 MA/cm2 in self field and liquid helium - are reached together with a very weak dependence on the magnetic field and a complete isotropy. Analysis through transmission electron microscopy evidences the presence of defects looking like lattice disorder at a very small scale, between 5 and 20 nm, which are thought to be responsible for such isotropic behavior in contrast to what was observed on SrTiO3, where defects parallel to the c-axis enhance pinning in that direction. © 2013 AIP Publishing LLC.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.