Films of FePt nanoparticles (NPs) embedded in MgO were obtained by controlled co-deposition of FePt NPs pre-formed by a gas aggregation source and of Mg evaporated in an oxygen atmosphere. Assemblies of core-shell FePt@MgO NPs and films of FePt NPs embedded in MgO matrix could be obtained by varying FePt and Mg deposition rates. Transmission electron microscopy (TEM) and high resolution-TEM revealed the core-shell structure of the NPs, with an FePt core (of average diameter ?d? = 4.75 nm) presenting a multitwinned icosahedral structure, and MgO partially in crystalline form. The functional effect of the MgO shell in shielding the FePt core from external oxidation was shown with XPS. Upon controlled annealing, a transition from A1 to L10 ordering could be obtained, with structural and morphological re-arrangement. The magnetic hysteresis loops obtained from alternating gradient field magnetometry at room temperature show a 'wasp-waist' shape, with small values of coercive field (Hc = 300-1400 Oe), decreasing at increasing amounts of co-deposited MgO.
Controlled co-deposition of FePt nanoparticles embedded in MgO: a detailed investigation of structure and electronic and magnetic properties
S D'Addato;V Grillo;A di Bona;P Luches;P Lupo;F Casoli;F Albertini
2013
Abstract
Films of FePt nanoparticles (NPs) embedded in MgO were obtained by controlled co-deposition of FePt NPs pre-formed by a gas aggregation source and of Mg evaporated in an oxygen atmosphere. Assemblies of core-shell FePt@MgO NPs and films of FePt NPs embedded in MgO matrix could be obtained by varying FePt and Mg deposition rates. Transmission electron microscopy (TEM) and high resolution-TEM revealed the core-shell structure of the NPs, with an FePt core (of average diameter ?d? = 4.75 nm) presenting a multitwinned icosahedral structure, and MgO partially in crystalline form. The functional effect of the MgO shell in shielding the FePt core from external oxidation was shown with XPS. Upon controlled annealing, a transition from A1 to L10 ordering could be obtained, with structural and morphological re-arrangement. The magnetic hysteresis loops obtained from alternating gradient field magnetometry at room temperature show a 'wasp-waist' shape, with small values of coercive field (Hc = 300-1400 Oe), decreasing at increasing amounts of co-deposited MgO.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.