The grafting of galactose units onto poly(e-caprolactone) (PCL) substrates by a wet chemistry two-step procedure is proposed. Even though a reduction of hardness from 0.58-0.31 GPa to 0.12-0.05 GPa is achieved, the chemical functionalization does not negatively affect the tensile modulus (332.2 ± 31.3 MPa and 328.5 ± 34.7 MPa for unmodified and surface-modified PCL, respectively) and strength (15.1 ± 1.3 MPa and 14.8 ± 1.5 MPa as assessed before and after the surface modification, respec- tively), as well as the mechanical behaviour evaluated through small punch test. XPS and enzyme-linked lectin assay (ELLA) demonstrate the presence, and also the correct exposition of the saccharidic epitope on PCL substrates. The introduction of carbohydrate moieties on the PCL surfaces clearly enhances the hydrophilicity of the substrate, as the water contact angle decreases from 82.1 ± 5.8 to 62.1 ± 4.2. Furthermore, preliminary biological analysis shows human mesenchymal stem cell viability over time and an improvement of cell adhesion and spreading.
Galactose grafting on poly(?-caprolactone) substrate for tissue engineering: a preliminary study
Teresa Russo;Antonio Gloria;Ugo D'Amora;Roberto De Santis;Luigi Ambrosio;
2014
Abstract
The grafting of galactose units onto poly(e-caprolactone) (PCL) substrates by a wet chemistry two-step procedure is proposed. Even though a reduction of hardness from 0.58-0.31 GPa to 0.12-0.05 GPa is achieved, the chemical functionalization does not negatively affect the tensile modulus (332.2 ± 31.3 MPa and 328.5 ± 34.7 MPa for unmodified and surface-modified PCL, respectively) and strength (15.1 ± 1.3 MPa and 14.8 ± 1.5 MPa as assessed before and after the surface modification, respec- tively), as well as the mechanical behaviour evaluated through small punch test. XPS and enzyme-linked lectin assay (ELLA) demonstrate the presence, and also the correct exposition of the saccharidic epitope on PCL substrates. The introduction of carbohydrate moieties on the PCL surfaces clearly enhances the hydrophilicity of the substrate, as the water contact angle decreases from 82.1 ± 5.8 to 62.1 ± 4.2. Furthermore, preliminary biological analysis shows human mesenchymal stem cell viability over time and an improvement of cell adhesion and spreading.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.