SrTi 0.7 Co 0.3 O 3, SrTi 0.7 Cu 0.3 O 3, SrTi 0.7 Co 0.15 Cu 0.15 O 3 were prepared by the "citrate route" and characterized (XRD, XPS, SEM, TPR). Their reactivity with respect to CO oxidation and NO reduction was investigated and compared with that of CuO/SrTi 0.7 Co 0.3 O 3 nanocomposite. High conversions were obtained in CO oxidation (90% at 350° C for SrTi 0.7 Co 0.3 O 3). Only CuO/SrTi 0.7 Co 0.3 O 3 was observed to be active in NO reduction (100% at 350° C)
Co- and Cu-doped titanates: Toward a new generation of catalytic converters
Natile M M;Vittadini A
2014
Abstract
SrTi 0.7 Co 0.3 O 3, SrTi 0.7 Cu 0.3 O 3, SrTi 0.7 Co 0.15 Cu 0.15 O 3 were prepared by the "citrate route" and characterized (XRD, XPS, SEM, TPR). Their reactivity with respect to CO oxidation and NO reduction was investigated and compared with that of CuO/SrTi 0.7 Co 0.3 O 3 nanocomposite. High conversions were obtained in CO oxidation (90% at 350° C for SrTi 0.7 Co 0.3 O 3). Only CuO/SrTi 0.7 Co 0.3 O 3 was observed to be active in NO reduction (100% at 350° C)File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
prod_296234-doc_85264.pdf
non disponibili
Descrizione: Co- and Cu-doped titanates: Toward a new generation of catalytic converters
Dimensione
599.58 kB
Formato
Adobe PDF
|
599.58 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.