Stoichiometric and partially reduced ceria films were deposited on preoxidized Ru(0001) crystal by Ce evaporation in oxygen atmosphere of different pressures at 700 K. Copper-ceria interaction was investigated by deposition of metalic copper on both types of substrate. The samples were characterized by low energy electron diffraction (LEED), X-ray photoelectron spectroscopy (XPS) of core states and resonant photoelectron spectroscopy (RPES) of the valence bands. Copper adsorption on stoichiometric ceria caused reduction of CeO2, while on the oxygen-defficient ceria it partially reoxidized the substrate. This is in agreement with DFT+U calculations of copper adsorption on stoichiometric and defective ceria surfaces. (C) 2012 Elsevier B. V. All rights reserved.
Copper-ceria interaction: A combined photoemission and DFT study
Fabris Stefano;Camellone Matteo Farnesi;
2013
Abstract
Stoichiometric and partially reduced ceria films were deposited on preoxidized Ru(0001) crystal by Ce evaporation in oxygen atmosphere of different pressures at 700 K. Copper-ceria interaction was investigated by deposition of metalic copper on both types of substrate. The samples were characterized by low energy electron diffraction (LEED), X-ray photoelectron spectroscopy (XPS) of core states and resonant photoelectron spectroscopy (RPES) of the valence bands. Copper adsorption on stoichiometric ceria caused reduction of CeO2, while on the oxygen-defficient ceria it partially reoxidized the substrate. This is in agreement with DFT+U calculations of copper adsorption on stoichiometric and defective ceria surfaces. (C) 2012 Elsevier B. V. All rights reserved.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.