As-synthesized organic-capped TiO2 nanorods were incorporated into polystyrene-block-poly(methyl methacrylate) (PS-b-PMMA) diblock copolymer to achieve TiO2/PS-b-PMMA nanocomposites with enhanced optical and conductive properties. The specific surface chemistry of TiO2 nanorods derived from the colloidal synthetic approach allowed their prompt incorporation in the PS-b-PMMA block copolymer template up to SO wt %, which resulted in films with an extended coverage of highly dispersed nanoparticles for contents higher than 30 wt %. At such high nanorod contents, the films fabricated by the prepared nanocomposites demonstrated enhanced optical properties. Atomic force microscopy investigation of the nanocomposite films showed a cylindrical morphology for low nanorod contents. Conversely, higher nanorod contents resulted upon removal of the organic component in the nanocomposites with UV treatment in overall nanorod coverage of the film surface with the concomitant formation of charge percolation paths, which led to noticeable conductivity values. EFM and PF-TUNA measurements confirmed the conductive properties of the composites at nanoscale, whereas semiconductor analyzer measurements provided their macroscale characterization. In addition, an increase in the UV-vis absorption was observed with the increase in the nanorod content along with a remarkable conductivity of the overall film.
Optical and conductive properties of as-synthesized organic-capped TiO 2 nanorods highly dispersible in polystyrene-block-poly(methyl methacrylate) diblock copolymer
Di Mauro Angela Evelyn;Striccoli Marinella;Curri Maria Lucia;
2014
Abstract
As-synthesized organic-capped TiO2 nanorods were incorporated into polystyrene-block-poly(methyl methacrylate) (PS-b-PMMA) diblock copolymer to achieve TiO2/PS-b-PMMA nanocomposites with enhanced optical and conductive properties. The specific surface chemistry of TiO2 nanorods derived from the colloidal synthetic approach allowed their prompt incorporation in the PS-b-PMMA block copolymer template up to SO wt %, which resulted in films with an extended coverage of highly dispersed nanoparticles for contents higher than 30 wt %. At such high nanorod contents, the films fabricated by the prepared nanocomposites demonstrated enhanced optical properties. Atomic force microscopy investigation of the nanocomposite films showed a cylindrical morphology for low nanorod contents. Conversely, higher nanorod contents resulted upon removal of the organic component in the nanocomposites with UV treatment in overall nanorod coverage of the film surface with the concomitant formation of charge percolation paths, which led to noticeable conductivity values. EFM and PF-TUNA measurements confirmed the conductive properties of the composites at nanoscale, whereas semiconductor analyzer measurements provided their macroscale characterization. In addition, an increase in the UV-vis absorption was observed with the increase in the nanorod content along with a remarkable conductivity of the overall film.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.