Compositi a matrice di alluminio rinforzati con nanoparticelle di allumina prodotti mediante un processo di metallurgia delle polveri = Aluminum matrix composites reinforced with alumina nanoparticles produced by a powder metallurgy route

Al wires reinforced with Al2O3 nanoparticles were produced by a powder metallurgy process, which relied on ball milling consolidation by extrusion and cold rolling. This procedure revealed to be able of preparing composites with a reinforcement homogeneously dispersed in a ultrafine grained microstructure. The ball milling was responsible of the fragmentation of the oxide layer which covered the Al powder particles and of the fracture of the alumina nanoclus-ters added ex situ. The nanocomposites showed improved mechanical properties in terms of hardness and tensile resistance. They also showed excellent damping properties at the high temperatures.

Sono stati prodotti fili di Al rinforzati con particelle nanometriche di Al2O3 mediante un processo di metallurgia delle polveri basato sulla macinazione severa e sulla consolidazione di polveri tramite estrusione a caldo. Le billette nanocomposite sono state infine laminate a freddo. Questa procedura ha consentito di preparare nanocompositi caratterizzati da un rinforzo nanometrico omogeneamente disperso in una matrice metallica a grani ultrafini. La macinazione ha provocato la frammentazione dell'ossido superficiale che copriva le particelle di Al e la rottura dei cluster di nano-allumina aggiunti ex situ. I nanocompositi mostrano proprietà meccaniche migliorate in termini di durezza e resistenza a trazione. Essi esibiscono inoltre eccellenti capacità di damping ad alta temperatura.