The influence of tin ions, complex [NiF6](2-), [SnF6](2-) ions on physico-chemical properties of lead dioxide electrodeposited from methanesulfonate electrolytes was studied. SEM images reveal a compact structure with round-shaped grains and X-ray diffractogramms demonstrated that incorporation of tin diminishes the size of crystal particles, while the incorporation of [NiF6](2-) causes the increasing of average crystal size. It is shown, that at low polarizations region the oxygen overpotential on micromodified PbO2-electrodes increases in the next line PbO2-[NiF6](2-) < PbO2-Sn4+ < PbO2 < PbO2-[SnF6](2-) and at high potentials the change of dependence occurs. (c) 2014 Elsevier B.V. All rights reserved.
Physico-chemical properties of PbO2-anodes doped with Sn4+ and complex ions
Amadelli R;
2014
Abstract
The influence of tin ions, complex [NiF6](2-), [SnF6](2-) ions on physico-chemical properties of lead dioxide electrodeposited from methanesulfonate electrolytes was studied. SEM images reveal a compact structure with round-shaped grains and X-ray diffractogramms demonstrated that incorporation of tin diminishes the size of crystal particles, while the incorporation of [NiF6](2-) causes the increasing of average crystal size. It is shown, that at low polarizations region the oxygen overpotential on micromodified PbO2-electrodes increases in the next line PbO2-[NiF6](2-) < PbO2-Sn4+ < PbO2 < PbO2-[SnF6](2-) and at high potentials the change of dependence occurs. (c) 2014 Elsevier B.V. All rights reserved.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.