A pre-patterning method of aluminium surface, in order to obtain highly ordered nanoporous anodized alumina on large areas is presented. Aluminium single crystals have been used as a substrate and a 2D hexagonally closed-packed lattice of shallow pits, with diameter of about 200 nm and period of 350 nm, has been successfully achieved by direct writing laser lithography (DWL) and wet etching. Finally, anodic oxidation of the single crystal at high cell voltage in phosphoric solution results in oxide growth with pore ordering superimposed by the pre-patterning procedure. © 2007 Elsevier B.V. All rights reserved.
Aluminium pre-patterning for highly ordered nanoporous anodized alumina
Pietralunga Silvia Maria
2007
Abstract
A pre-patterning method of aluminium surface, in order to obtain highly ordered nanoporous anodized alumina on large areas is presented. Aluminium single crystals have been used as a substrate and a 2D hexagonally closed-packed lattice of shallow pits, with diameter of about 200 nm and period of 350 nm, has been successfully achieved by direct writing laser lithography (DWL) and wet etching. Finally, anodic oxidation of the single crystal at high cell voltage in phosphoric solution results in oxide growth with pore ordering superimposed by the pre-patterning procedure. © 2007 Elsevier B.V. All rights reserved.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.