Luminescent CdS nanocrystals embedded in a polystyrene matrix were successfully prepared. The in situ growth of CdS QDs was realized by thermal treatment of Cd bis(thiolate)/polymer foil at different times and temperatures (240 degrees C and 300 degrees C) of annealing, in order to evaluate their influence on the quantum dots growth process. As a general trend, the increasing of time and temperature of annealing induces a rise of the CdS nanocrystals size into the polymeric matrix. The size distribution, morphology, and structure of the CdS nanoparticles were analysed with HRTEM and XRD experiments. UV-Vis and PL data are strongly size-dependent and were used to investigate the particles' growth process, too. The CdS nanoparticles behavior in solution indicated a general trend of QDs to aggregation. This predisposition was clearly displayed by DLS measurements.
Time and Temperature Dependence of CdS Nanoparticles Grown in a Polystyrene Matrix
Morandi V;Ortolani L;Accorsi G;Blosi M
2012
Abstract
Luminescent CdS nanocrystals embedded in a polystyrene matrix were successfully prepared. The in situ growth of CdS QDs was realized by thermal treatment of Cd bis(thiolate)/polymer foil at different times and temperatures (240 degrees C and 300 degrees C) of annealing, in order to evaluate their influence on the quantum dots growth process. As a general trend, the increasing of time and temperature of annealing induces a rise of the CdS nanocrystals size into the polymeric matrix. The size distribution, morphology, and structure of the CdS nanoparticles were analysed with HRTEM and XRD experiments. UV-Vis and PL data are strongly size-dependent and were used to investigate the particles' growth process, too. The CdS nanoparticles behavior in solution indicated a general trend of QDs to aggregation. This predisposition was clearly displayed by DLS measurements.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.