Crystal shape control on a series of anatase photocatalysts was achieved by varying the amount of HF employed as a capping agent in their hydrothermal synthesis. A systematic comparison between their physicochemical properties, determined by several complementary surface and bulk techniques before and after thermal treatment at 500 °C, allowed one to discern the influence of the relative amount of exposed {001} crystal facets among a series of effects simultaneously affecting their oxidative photocatalytic activity. The results of both formic acid and terephthalic acid photo-oxidation test reactions point to the primary role played by calcination in making {001} facets effectively photoactive. Annealing not only removes most of the residual fluorine capping agent from the photocatalyst surface, thus favoring substrate adsorption, but also produces morphological modifications to a crystal packing that makes accessible a larger portion of surface {001} facets due to the unpiling of platelike crystals. The photocatalyst bearing the highest amount of exposed {001} facets (60%) shows the highest photoactivity in both the direct and the oOH-radical-mediated photocatalytic test reaction.
Unraveling the Multiple Effects Originating the Increased Oxidative Photoactivity of {001}-Facet Enriched Anatase TiO2
Coduri M;
2016
Abstract
Crystal shape control on a series of anatase photocatalysts was achieved by varying the amount of HF employed as a capping agent in their hydrothermal synthesis. A systematic comparison between their physicochemical properties, determined by several complementary surface and bulk techniques before and after thermal treatment at 500 °C, allowed one to discern the influence of the relative amount of exposed {001} crystal facets among a series of effects simultaneously affecting their oxidative photocatalytic activity. The results of both formic acid and terephthalic acid photo-oxidation test reactions point to the primary role played by calcination in making {001} facets effectively photoactive. Annealing not only removes most of the residual fluorine capping agent from the photocatalyst surface, thus favoring substrate adsorption, but also produces morphological modifications to a crystal packing that makes accessible a larger portion of surface {001} facets due to the unpiling of platelike crystals. The photocatalyst bearing the highest amount of exposed {001} facets (60%) shows the highest photoactivity in both the direct and the oOH-radical-mediated photocatalytic test reaction.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.