Innovative hydrophobic coated membranes have been prepared and characterized in Direct Contact Membrane Distillation (DCMD) for potential water treatment applications. A UV-curable per- fluoropolyether(PFPE) hydrophobic compound(Fluorolinks AD 1700) was used as coating material to tailor the surface of commercial micro filtration hydrophilic polyamide(PA) membranes with different pore sizes. The coated membranes consisted of a top thin hydrophobic porous layer overlying the hydrophilic commercial membrane support. Produced membranes were fully characterized in terms of surface and cross-section morphology, water contact angle, porosity, pore size and liquid entry pressure.The in- novative coated hydrophobic membranes were tested in DCMD configuration, using deionized water and salty solution 0.6M(NaCl) as feed. In particular,the effect of the coating concentration on the permeate fluxes was investigated for different hydrophilic pore size commercial membranes (0.1-0.22-0.45 ?m). The measured permeate fluxes ranged between 4.56-22.81 kg/m2 h at different feed temperatures(40- 50-60 °C) keeping constant the permeate temperature at 14 °C, for deionized water, whereas an average value of 11kg/m2 h, at 50 °C was found in case of the salty solution.
Innovative hydrophobic coating of perfluoropolyether (PFPE) on commercial hydrophilic membranes for DCMD application
Figoli A;Ursino C;Galiano F;Carnevale MC;Criscuoli A
2017
Abstract
Innovative hydrophobic coated membranes have been prepared and characterized in Direct Contact Membrane Distillation (DCMD) for potential water treatment applications. A UV-curable per- fluoropolyether(PFPE) hydrophobic compound(Fluorolinks AD 1700) was used as coating material to tailor the surface of commercial micro filtration hydrophilic polyamide(PA) membranes with different pore sizes. The coated membranes consisted of a top thin hydrophobic porous layer overlying the hydrophilic commercial membrane support. Produced membranes were fully characterized in terms of surface and cross-section morphology, water contact angle, porosity, pore size and liquid entry pressure.The in- novative coated hydrophobic membranes were tested in DCMD configuration, using deionized water and salty solution 0.6M(NaCl) as feed. In particular,the effect of the coating concentration on the permeate fluxes was investigated for different hydrophilic pore size commercial membranes (0.1-0.22-0.45 ?m). The measured permeate fluxes ranged between 4.56-22.81 kg/m2 h at different feed temperatures(40- 50-60 °C) keeping constant the permeate temperature at 14 °C, for deionized water, whereas an average value of 11kg/m2 h, at 50 °C was found in case of the salty solution.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.