The galvanic exchange between Mn2+ ions and electrodeposited porous PbO2 was studied to produce a porous oxide whose lower conductivity prevented its direct oxygen bubble-templated anodic deposition. Immersion of PbO2 layers in acid acetate solutions of Mn2+ led to the formation of amorphousMnOx shell onto PbO2. Due to its amorphous nature, MnOx could not be proved to be MnO2 by XRD. However, MnOx was cathodically stripped at the same potential as MnO2. The deposition of the MnOx shell onto PbO2 enhanced the capacity of the porous electrodes.
Conversion of porous PbO2 layers through galvanic displacement reaction with Mn2+ ions
Comisso N;Cattarin S;Guerriero P;Mattarozzi L;Musiani M;Verlato E
2016
Abstract
The galvanic exchange between Mn2+ ions and electrodeposited porous PbO2 was studied to produce a porous oxide whose lower conductivity prevented its direct oxygen bubble-templated anodic deposition. Immersion of PbO2 layers in acid acetate solutions of Mn2+ led to the formation of amorphousMnOx shell onto PbO2. Due to its amorphous nature, MnOx could not be proved to be MnO2 by XRD. However, MnOx was cathodically stripped at the same potential as MnO2. The deposition of the MnOx shell onto PbO2 enhanced the capacity of the porous electrodes.File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
prod_360415-doc_120022.pdf
solo utenti autorizzati
Descrizione: Conversion of porous PbO2 layers through galvanic displacement reaction with Mn2 + ions
Tipologia:
Versione Editoriale (PDF)
Dimensione
713.76 kB
Formato
Adobe PDF
|
713.76 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.