This work is focused on the design and development of hybrid solid-state energy storage devices with high capacitive performance. In particular, the work includes, the preparation of carbon composite electrodes based on a carbon nanofibers (CNF) supported on a cotton fabric. The coating of CNF to the cotton cloth is obtained by the dip and dry method. On these so-obtained composite substrates, further layers of activated carbon (Norit A Supra Eur) and manganese oxide (MnO2) material have been subsequenlty deposited to enhance the electrochemical performances of negative and positive electrodes, respectively. The preparation of carbon-based active layers comprises the spreading on the negative CNF-substrate of a slurry containing the activated carbon (AC) material, graphite fibres and polyvinylidene difluoride (PVDF) in N,N dimethylacetamide (DMA). Whereas the positive electrode is prepared by spreading a slurry of MnO2, carbon black, graphite fibers, PVDF in DMA. A 1M Na2SO4 solution impregnated in the porous paper separator (Nippon Kodoshi Corportion, Japan) and a polymer electrolyte membrane (Nafion 115) have been employed as electrolytes. The different supercapacitors were electrochemically characterized by cyclic voltammetry (CV), galvanostatic charge/discharge (G-CD), electrochemical impedance spectroscopy (EIS) and long-term cycling stability tests. The hybrid carbon-based textile supercapacitors exhibited capacitance performance of 137 and 120 F/g with the porous separator and Nafion 115 membrane, respectively. Specially, the solid-state (Nafion membrane) hybrid device demonstrated very long stability in cycling (10000 cycles) and voltage holding conditions at 1.6 V (more than 100 h). Besides, these textile-based capacitors also showed slow self-discharge. Acknowledgments This work was partly financed by FEDER funds through the Competitivity Factors Operational Programme - COMPETE and by national funds through FCT - Foundation for Science and Technology (project POCI-01-0145-FEDER-007136). A. J. Paleo acknowledges the European COST Action CA15107- Multi-Functional Nano-Carbon Composite Materials Network (MultiComp) that conceded a Short Term Scientific Mission (STSM) at CNR-ITAE of Messina.
Carbon and MnO2 materials on carbon nanofibers cotton textile substrate for hybrid solid-state supercapacitors
F Lufrano;P Staiti
2017
Abstract
This work is focused on the design and development of hybrid solid-state energy storage devices with high capacitive performance. In particular, the work includes, the preparation of carbon composite electrodes based on a carbon nanofibers (CNF) supported on a cotton fabric. The coating of CNF to the cotton cloth is obtained by the dip and dry method. On these so-obtained composite substrates, further layers of activated carbon (Norit A Supra Eur) and manganese oxide (MnO2) material have been subsequenlty deposited to enhance the electrochemical performances of negative and positive electrodes, respectively. The preparation of carbon-based active layers comprises the spreading on the negative CNF-substrate of a slurry containing the activated carbon (AC) material, graphite fibres and polyvinylidene difluoride (PVDF) in N,N dimethylacetamide (DMA). Whereas the positive electrode is prepared by spreading a slurry of MnO2, carbon black, graphite fibers, PVDF in DMA. A 1M Na2SO4 solution impregnated in the porous paper separator (Nippon Kodoshi Corportion, Japan) and a polymer electrolyte membrane (Nafion 115) have been employed as electrolytes. The different supercapacitors were electrochemically characterized by cyclic voltammetry (CV), galvanostatic charge/discharge (G-CD), electrochemical impedance spectroscopy (EIS) and long-term cycling stability tests. The hybrid carbon-based textile supercapacitors exhibited capacitance performance of 137 and 120 F/g with the porous separator and Nafion 115 membrane, respectively. Specially, the solid-state (Nafion membrane) hybrid device demonstrated very long stability in cycling (10000 cycles) and voltage holding conditions at 1.6 V (more than 100 h). Besides, these textile-based capacitors also showed slow self-discharge. Acknowledgments This work was partly financed by FEDER funds through the Competitivity Factors Operational Programme - COMPETE and by national funds through FCT - Foundation for Science and Technology (project POCI-01-0145-FEDER-007136). A. J. Paleo acknowledges the European COST Action CA15107- Multi-Functional Nano-Carbon Composite Materials Network (MultiComp) that conceded a Short Term Scientific Mission (STSM) at CNR-ITAE of Messina.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.