Ashes derived from the combustion of vegetal and animal biomass still represent a mostly unexplored secondary raw material for the production of alkali-activated materials, given their peculiar chemical nature. In this work, calcium phosphate biomass ashes were successfully used as partially reactive fillers in a metakaolin-based geopolymer composite to produce, by direct foaming, sustainable and lightweight boards with thermal insulating properties. The investigated materials were obtained by activating a blend of metakaolin and biomass ash in a weight ratio of 1: 1 and foamed with the addition of H2O2 in measure of 5 wt. %, to maximize the volume of disposed ash and ensure adequate properties to the material at the same time. The obtained geopolymer composite was characterized by microstructural, chemical-physical, mechanical and thermal analysis: the obtained results showed that biomass ash and metakaolin well integrated in the microstructure of the final porous material, which was characterized by a density of about 310 kg/m3 and a thermal conductivity of 0.073 W/mK at a mean test temperature of 30 °C, coupled with an acceptable compressive strength of about 0.6 MPa. Dilatometric and thermogravimetric analysis, performed up to 1000 °C, highlighted the thermal stability of the composite, which could be regarded as a promising material for low-cost, self-bearing thermal insulating partitions or lightweight cores for thermostructural sandwich panels.
Porous Geopolymer Insulating Core from a Metakaolin/Biomass Ash Composite
A Natali Murri
Primo
;V MedriSecondo
;E Papa;E LandiUltimo
2017
Abstract
Ashes derived from the combustion of vegetal and animal biomass still represent a mostly unexplored secondary raw material for the production of alkali-activated materials, given their peculiar chemical nature. In this work, calcium phosphate biomass ashes were successfully used as partially reactive fillers in a metakaolin-based geopolymer composite to produce, by direct foaming, sustainable and lightweight boards with thermal insulating properties. The investigated materials were obtained by activating a blend of metakaolin and biomass ash in a weight ratio of 1: 1 and foamed with the addition of H2O2 in measure of 5 wt. %, to maximize the volume of disposed ash and ensure adequate properties to the material at the same time. The obtained geopolymer composite was characterized by microstructural, chemical-physical, mechanical and thermal analysis: the obtained results showed that biomass ash and metakaolin well integrated in the microstructure of the final porous material, which was characterized by a density of about 310 kg/m3 and a thermal conductivity of 0.073 W/mK at a mean test temperature of 30 °C, coupled with an acceptable compressive strength of about 0.6 MPa. Dilatometric and thermogravimetric analysis, performed up to 1000 °C, highlighted the thermal stability of the composite, which could be regarded as a promising material for low-cost, self-bearing thermal insulating partitions or lightweight cores for thermostructural sandwich panels.File | Dimensione | Formato | |
---|---|---|---|
prod_379438-doc_128506.pdf
accesso aperto
Descrizione: articolo pubblicato
Tipologia:
Versione Editoriale (PDF)
Licenza:
Creative commons
Dimensione
2.97 MB
Formato
Adobe PDF
|
2.97 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.