The bulk transport properties of positive carriers in thin films of a low band-gap conjugated polymer, called APFO-Green5, have been investigated in the ac regime. The frequency-dependent impedance of an ITO/PEDOT:PSS/APFO-Green5/Al structure (where ITO is indium tin oxide and PEDOT:PSS is poly(3,4-ethylenedioxythiophene)/polystyrene sulphonic acid) was measured as a function of the dc applied bias. The capacitance response at low frequency gave indication of a combination of trapping and double-injection effects, while in the intermediate-high frequency range was determined by the transit time of injected holes. Hole mobility in APFO-Green5 thin films exhibited a Frenkel-like dependence on the applied electric field, with a field-dependent coefficient of around 8 x 10(-3) (V cm(-1))(-1/2). A hole mobility close to 2 x 10(-5) cm(2) V-1 s(-1) was achieved at the field of 3.5 x 10(5) V cm(-1), in excellent agreement with that already reported by using a different bulk investigation technique.
Hole-transport properties of a low-band gap alternating polyfluorene
2010
Abstract
The bulk transport properties of positive carriers in thin films of a low band-gap conjugated polymer, called APFO-Green5, have been investigated in the ac regime. The frequency-dependent impedance of an ITO/PEDOT:PSS/APFO-Green5/Al structure (where ITO is indium tin oxide and PEDOT:PSS is poly(3,4-ethylenedioxythiophene)/polystyrene sulphonic acid) was measured as a function of the dc applied bias. The capacitance response at low frequency gave indication of a combination of trapping and double-injection effects, while in the intermediate-high frequency range was determined by the transit time of injected holes. Hole mobility in APFO-Green5 thin films exhibited a Frenkel-like dependence on the applied electric field, with a field-dependent coefficient of around 8 x 10(-3) (V cm(-1))(-1/2). A hole mobility close to 2 x 10(-5) cm(2) V-1 s(-1) was achieved at the field of 3.5 x 10(5) V cm(-1), in excellent agreement with that already reported by using a different bulk investigation technique.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.