The corrosion behaviour of oxide dispersion strengthened (ODS) steels with different chromium contents (9, 12 and 14 wt% Cr) is investigated in stagnant liquid lead at a temperature of 973 K for 2000 h. Under an oxygen concentration close to the passivation domain (i.e. Co ~10-5-10-4 wt% O), neither an internal oxidation zone in the steel matrix, nor dissolution attack caused by liquid lead or its penetration is observed. Indeed, thin layers of chromium rich oxides with different compositions are detected.
Corrosion behaviour of oxide dispersion strengthened iron-chromium steels in liquid lead at 973 K
Ricci E;Giuranno D;Canu G;Amore S;Novakovic R
2018
Abstract
The corrosion behaviour of oxide dispersion strengthened (ODS) steels with different chromium contents (9, 12 and 14 wt% Cr) is investigated in stagnant liquid lead at a temperature of 973 K for 2000 h. Under an oxygen concentration close to the passivation domain (i.e. Co ~10-5-10-4 wt% O), neither an internal oxidation zone in the steel matrix, nor dissolution attack caused by liquid lead or its penetration is observed. Indeed, thin layers of chromium rich oxides with different compositions are detected.File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
prod_393683-doc_136222.pdf
solo utenti autorizzati
Descrizione: Corrosion behaviour of oxide dispersion strengthened iron-chromium steels in liquid lead at 973 K
Tipologia:
Versione Editoriale (PDF)
Dimensione
1.64 MB
Formato
Adobe PDF
|
1.64 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.