The foamability of miscible blends based on semicrystalline Poly(ether ether ketone) - PEEK and amorphous Poly(ether imide) - PEI have been investigated for their potential outstanding mechanical, thermal and chemical-physical specific properties with the aim to produce high performance foams with a microcellular or sub-microcellular morphology and low density. Foams have been obtained by using supercritical carbon dioxide as blowing agent and were prepared by means of the solid state foaming technique, which uses a fast temperature increase to induce bubbles nucleation and growth in samples previously solubilized with the blowing agent. The role of blend composition, solubilization pressure, and crystallinity on density and morphological parameters of the resulting foams has been investigated. A closed cell microcellular morphology, with average cell size between 0.9 and 2.3 mu m, was obtained and nucleated bubbles up to 10(12) cells cm(-3) were detected. Higher CO2 uptake allowed a decrease of the foam density at each foaming temperature (down to 0.13 g cm(-3)), while a complex relationship between foaming temperature and cellular morphology (in terms of nucleated cells and mean cell size) emerged. (C) 2016 Elsevier Ltd. All rights reserved.
Microcellular foams from high performance miscible blends based on PEEK and PEI
Cafiero Livia;Iannace Salvatore;Sorrentino Luigi
2016
Abstract
The foamability of miscible blends based on semicrystalline Poly(ether ether ketone) - PEEK and amorphous Poly(ether imide) - PEI have been investigated for their potential outstanding mechanical, thermal and chemical-physical specific properties with the aim to produce high performance foams with a microcellular or sub-microcellular morphology and low density. Foams have been obtained by using supercritical carbon dioxide as blowing agent and were prepared by means of the solid state foaming technique, which uses a fast temperature increase to induce bubbles nucleation and growth in samples previously solubilized with the blowing agent. The role of blend composition, solubilization pressure, and crystallinity on density and morphological parameters of the resulting foams has been investigated. A closed cell microcellular morphology, with average cell size between 0.9 and 2.3 mu m, was obtained and nucleated bubbles up to 10(12) cells cm(-3) were detected. Higher CO2 uptake allowed a decrease of the foam density at each foaming temperature (down to 0.13 g cm(-3)), while a complex relationship between foaming temperature and cellular morphology (in terms of nucleated cells and mean cell size) emerged. (C) 2016 Elsevier Ltd. All rights reserved.File | Dimensione | Formato | |
---|---|---|---|
prod_397905-doc_165912.pdf
solo utenti autorizzati
Descrizione: Microcellular foams from high performance miscible blends based on PEEK and PEI
Tipologia:
Versione Editoriale (PDF)
Dimensione
3.58 MB
Formato
Adobe PDF
|
3.58 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
prod_397905-doc_185222.pdf
accesso aperto
Descrizione: Microcellular foams from high performance miscible blends based on PEEK and PEI
Tipologia:
Versione Editoriale (PDF)
Dimensione
172.03 kB
Formato
Adobe PDF
|
172.03 kB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.