Dislocation-density-related equations were proved to be promising tools to correlate tensile plastic behaviour and microstructure in ductile irons (DIs), revealing distinct relationships between equation parameters and microstructure features in austempered ductile irons (ADI) and isothermed ductile irons (IDI). These equations resulted to be successful also in the characterization of the austempering process through the plastic behaviour analysis of tensile tests of an ADI 1050 that was quenched at different times during austempering. The equation parameters could indeed be correlated to the time window for the best ausferrite, and could predict the precipitation of the deleterious epsilon' carbides for long austempering times. In the present work the results of the tensile plastic behaviour analysis of different DIs through dislocation-density-related equations are reported. The aim of the analysis was to test the capability of these equations to assess the microstructure quality of DIs and support their industrial production.
Evaluation of Microstructure Quality in Ductile Irons Based on Tensile Behaviour Analysis
Donnini R;Angella G
2018
Abstract
Dislocation-density-related equations were proved to be promising tools to correlate tensile plastic behaviour and microstructure in ductile irons (DIs), revealing distinct relationships between equation parameters and microstructure features in austempered ductile irons (ADI) and isothermed ductile irons (IDI). These equations resulted to be successful also in the characterization of the austempering process through the plastic behaviour analysis of tensile tests of an ADI 1050 that was quenched at different times during austempering. The equation parameters could indeed be correlated to the time window for the best ausferrite, and could predict the precipitation of the deleterious epsilon' carbides for long austempering times. In the present work the results of the tensile plastic behaviour analysis of different DIs through dislocation-density-related equations are reported. The aim of the analysis was to test the capability of these equations to assess the microstructure quality of DIs and support their industrial production.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.