Ni- and Ru-based catalytic pellets supported on commercial -Al2O3 pellets modified with magnesium oxide have been prepared for application in the catalytic conversion of ethanol into butanol. MgO/-Al2O3 pellets with or without added metals have been characterized by XRD, SEM/EDX, TGA, N-2 physisorption, H-2 TPR, and CO2 TPD in order to investigate the effect of MgO coverage and metal distribution on the surface and red-ox properties of the materials and, in turn, their effects on the catalytic performance. The conversion of ethanol into butanol has been investigated in a continuous flow reactor at 350-400 degrees C under diluted conditions (3% ethanol) in order to rank the different catalytic pellets and identify the best formulations and preparation procedures via a comparison with powder catalysts previously proposed in the literature with similar compositions. Results show enhanced catalytic performance for MgO-covered alumina pellets with respect to a pure MgO powder catalyst in spite of the lower MgO load. A significant further positive effect is found when Ni or Ru enters a solid solution with MgO.
Ni or Ru supported on MgO/-Al2O3 pellets for the catalytic conversion of ethanol into butanol
Apuzzo J;Cimino S;Lisi L
2018
Abstract
Ni- and Ru-based catalytic pellets supported on commercial -Al2O3 pellets modified with magnesium oxide have been prepared for application in the catalytic conversion of ethanol into butanol. MgO/-Al2O3 pellets with or without added metals have been characterized by XRD, SEM/EDX, TGA, N-2 physisorption, H-2 TPR, and CO2 TPD in order to investigate the effect of MgO coverage and metal distribution on the surface and red-ox properties of the materials and, in turn, their effects on the catalytic performance. The conversion of ethanol into butanol has been investigated in a continuous flow reactor at 350-400 degrees C under diluted conditions (3% ethanol) in order to rank the different catalytic pellets and identify the best formulations and preparation procedures via a comparison with powder catalysts previously proposed in the literature with similar compositions. Results show enhanced catalytic performance for MgO-covered alumina pellets with respect to a pure MgO powder catalyst in spite of the lower MgO load. A significant further positive effect is found when Ni or Ru enters a solid solution with MgO.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.