Local dielectric spectroscopy, which entails measuring the change in resonance frequency of the conducting tip of an atomic force microscope to determine the complex permittivity of a sample with high spatial (lateral) resolution, was employed to characterize the dynamics of thin films of poly(vinyl methyl ketone) (PVMK) having different substrate and top surface layers. A free surface yields the usual speeding up of the segmental dynamics, corresponding to a glass transition suppression of 6.5° for 18 nm film thickness. This result is unaffected by the presence of a glassy, compatible polymer, poly-4-vinyl phenol (PVPh), between the metal substrate and the PVMK. However, covering the top surface with a thin layer of the PVPh suppresses the dynamics. The speeding up of PVMK segmental motions observed for a free surface is absent due to interfacial interactions of the PVMK with the glass layer, an effect not seen when the top layer is an incompatible polymer.
Dynamics of poly(vinyl methyl ketone) thin films studied by local dielectric spectroscopy
Labardi M;
2017
Abstract
Local dielectric spectroscopy, which entails measuring the change in resonance frequency of the conducting tip of an atomic force microscope to determine the complex permittivity of a sample with high spatial (lateral) resolution, was employed to characterize the dynamics of thin films of poly(vinyl methyl ketone) (PVMK) having different substrate and top surface layers. A free surface yields the usual speeding up of the segmental dynamics, corresponding to a glass transition suppression of 6.5° for 18 nm film thickness. This result is unaffected by the presence of a glassy, compatible polymer, poly-4-vinyl phenol (PVPh), between the metal substrate and the PVMK. However, covering the top surface with a thin layer of the PVPh suppresses the dynamics. The speeding up of PVMK segmental motions observed for a free surface is absent due to interfacial interactions of the PVMK with the glass layer, an effect not seen when the top layer is an incompatible polymer.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.